September 22, 2021
Additive Manufacturing company Uniformity Labs (Uniformity) has successfully printed an additively designed automotive component with its ultra-low porosity AlSi10Mg, a high throughput, aluminum alloy powder that exhibits best-in-class material properties. The Uniformity AlSi10Mg powder and optimizing print processes have previously been deployed with a variety of parts in various industries with great success.
In its latest application, Uniformity produced a roll-cage designed for a solar powered race car on an in-house SLM 280 2.0 Dual Laser Powder Bed Fusion 3D printer. The part will be used on a car participating in the Bridgestone World Solar Challenge, an international event for solar-powered cars driving 3000 kilometers through the Australian outback.
The roll cage was printed with a 30um layer thickness to get a fantastic surface finish from the printer with best-in-class mechanical properties and the added benefit of delivering the productivity level of a 60um layer thickness print. Uniformity brings No Compromise Metal Additive Manufacturing to the industry with its material and print solutions.
The car engineering team used topological optimization techniques to design the part to ensure strength while reducing material usage (weight). The cost and material performance were critical factors, so they replaced carbon fiber with an additive manufactured part made from the Uniformity AlSi10Mg powder. This application of our material also demonstrates its advantage in furthering the future of sustainable mobility, where robust, lightweight parts are required to accelerate the transition to cleaner, safer, more inclusive mobility systems.
This is an excellent example of how our innovation can significantly improve part design using our advanced powders and modern AM techniques,” said Adam Hopkins, founder and CEO of Uniformity Labs. “Our ultra-low porosity AlSi10Mg and print processes allowed the car development team to create a better part quickly, cheaply, and optimized for the necessary weight and safety parameters.”
“It’s easy to see how the processes used, and benefits afforded to the roll-cage production can apply to the creation of complex parts for use in mainstream industries such as aviation, auto, and consumer electronics,” Hopkins continued. “That’s what our technology is all about.”
AlSi10Mg Mechanical and Density Information
At a glance mechanical and density properties listed below (as built/stress relieved annealed)
30um layer thicknessThree times the throughput @ 99.8%+ density (average 99.9%)Ultimate Tensile Strength (Rm z) – 406 ± 14 MPa/ 251 ± 8 MPaUltimate Tensile Strength (Rm xy) – 438 ± 18 MPa/ 247 ± 9 MPaYield Strength (Rm z) 264 ± 8 MPa/148 ± 5Yield Strength (Rm xy) 291 ± 12 MPa/156 ± 4Fracture Elongation (Rm z) 3.7 ± 0.7%/14.2 ± 1.1%Fracture Elongation (Rm xy) 7.2 ± 1.1%/17.3 ± 2.0%Surface roughness in z direction (no treatment) (um) 3.4 ± 0.9
Coupon Type: ASTM E8/E8-M Rectangular Tension Test Specimens, Subsize (25mm gauge), no polishingFor a complete data sheet, please email: firstname.lastname@example.org
Uniformity Labs develops breakthrough material and software solutions to accelerate and expand global commercial/industrial 3D printing (AM) markets. Its patented technology uniquely enables fully dense printing with minimal shrinkage of binder jetting materials, delivering significant cost savings, speed, and quality improvements across all mainstream AM printers. Uniformity’s feedstock materials and print processes dramatically impact the AM value chain by increasing the reliability and efficiency of printing.
For more information please visit our website – www.uniformitylabs.com
Frank De Maria – 347-647-0284
Uniformity Labs (Uniformity), a leading additive manufacturing (AM) company that is revolutionizing industrial 3D printing
Complementary technological capabilities allow customers to achieve higher quality, greener, more sustainable part production. March
Engineered materials company Uniformity Labs (Uniformity) announces the availability of titanium alloy Ti-6Al-4V (Ti64) powder